TRL CAST LC 80

FURMATS offer wide range of Low Cement (LC) Castables ranging from 45% Alumina to 90% Alumina for applications in Cement Kiln, DRI kiln, Incinerators, Tundish, Alumina Kiln, Rotary Kiln, Striker Pads, Launders, Snorkel of RH unit, etc. We offer TRL Cast LC 80, 80% Al2O3 ,Bauxite based low cement castable Maximum Service temperature 1600°C.
Application: DRI Kiln, Alumina Kiln, lances.
Product Description: 60% Al2O3 low cement castable
PRODUCT DESCRIPTION
Bauxite based low cement castable
APPLICATION
Cement Kiln, DRI kiln, Incinerators, Tundish, Alumina Kiln, Rotary Kiln, Striker Pads, Launders, Snorkel of RH unit, etc.
CONTROL PROPERTIES
Product Definition Sheet |
TRL Cast LC 80 Castable |
|||||
Product Name |
TRL Cast LC 80 |
|||||
Product Description |
Bauxite based low cement castable |
|||||
Maximum Service temperature |
1600°C |
|||||
CONTROL PROPERTIES |
||||||
Chemical Analysis |
Unit by wt |
Value |
Test Method |
|||
Typical |
Limit |
|||||
Al2O3 |
% |
80.6 |
≥ 80 |
By XRF |
||
Fe2O3 |
% |
1.38 |
≤ 1.5 |
By XRF |
||
CaO |
% |
2.11 |
By XRF |
|||
Physical properties |
Unit |
|||||
Bulk Density at 110oC/24 hrs |
Kg/m3 |
2750 |
≥ 2700 |
BIS 10570 |
||
CCS at 110°C/24 hrs |
N/mm2 |
87 |
≥ 80 |
BIS 10570 |
||
CCS at 800°C/3 hrs |
N/mm2 |
99 |
≥ 90 |
BIS 10570 |
||
CCS at 1100°C/3 hrs |
N/mm2 |
112 |
≥ 100 |
BIS 10570 |
||
CCS at 1500°C/3 hrs |
N/mm2 |
134 |
≥ 120 |
BIS 10570 |
||
PCE |
°C |
+ 1800 |
≥ 1800 |
BIS – 1528 |
||
Thermal conductivity |
||||||
At 400oC hot face |
W/mk |
1.98 |
BIS 9490 |
|||
At 600oC hot face |
W/mk |
2.05 |
BIS 9490 |
|||
At 800oC hot face |
W/mk |
2.17 |
BIS 9490 |
|||
PLC at 1100°C/3 hrs |
% |
– 0.26 |
ASTM C113-1993 |
|||
PLC at 1550°C/3 hrs |
% |
– 0.77 |
≤ +/- 1.0 |
ASTM C113-1993 |
||
Maximum Grain size |
mm |
98.7% passing through 5 mm |
≤ 5 |
|||
Shelf Life |
6 months from the date of manufacture |
|||||